Synthesis of goethite (α-FeOOH) pigment by precipitation method from iron lathe waste

lilik miftahul, khoiroh and Elysia Dwi, Nuraini and Nur, Aini (2018) Synthesis of goethite (α-FeOOH) pigment by precipitation method from iron lathe waste. alchemy, Vol 6 (2). pp. 65-69. ISSN e-Issn 2460-6871

[img]
Preview
Text (fulltext)
geothite.pdf - Published Version
Available under License Creative Commons Attribution Non-commercial Share Alike.

Download (403kB) | Preview
Full text available at: http://ejournal.uin-malang.ac.id/index.php/Kimia/a...

Abstract

Lathe waste contains high iron content potential to be further processed into goethite pigment. The purpose of the research was to determine the effect of synthesis temperature on the structure, colour values, and morphology of goethite pigment. The synthesis was conducted with temperature variations of 60, 70, 80 and 90°C. The XRD diffraction pattern shows that crystal structure of the product of all synthesis temperatures are goethite (α-Fe-OOH) with orthorhombic structure. The crystal size of the pigment ranges between 11.17 – 12.32 nm. Colour value analysis shows that product of 70°C synthesis temperature exhibits the highest lightness value about 40.5. Based on SEM-EDX imaging, the morphology of the samples is not uniform and forming agglomerates. Traces of impurities were detected, such as C and Na.

Item Type: Journal Article
Keywords: Iron lathe waste, goethite, temperature, precipitation
Subjects: 03 CHEMICAL SCIENCES > 0302 Inorganic Chemistry > 030201 Bioinorganic Chemistry
Divisions: Faculty of Mathematics and Sciences > Department of Chemistry
Depositing User: lilik miftahul khoiroh
Date Deposited: 10 May 2020 01:06

Downloads

Downloads per month over past year

Origin of downloads

Actions (login required)

View Item View Item