Tensile strength and elongation analysis on nano cellulose film isolated from sugarcane bagasse

Yuwono, M., Fauziyah, Begum, Isnaeni, Isnaeni and Nisak, A. (2020) Tensile strength and elongation analysis on nano cellulose film isolated from sugarcane bagasse. Presented at The 10th International Conference on Green Technology (ICGT) "Empowering the Fourth Industrial Revolution through Green Science and Technology", 2-3 Oct 2019, Malang.

[img]
Preview
Text
8733.pdf - Published Version
Available under License Creative Commons Attribution.

Download (918kB) | Preview

Abstract

Nano cellulose was successfully isolated from sugarcane bagasse through sulphuric acid hydrolysis of sugarcane bagasse cellulose. Physically, Nano cellulose was transparent and broken white. The crystallinity index of sugarcane bagasse nano cellulose was 80.72%. The particle size of sugarcane bagasse nano cellulose was 225 nm. Delignification process in isolation was successfully showed by releasing peaks in 1239.3 and 1507.7. It show C-O-C vibration of aryl group in lignin and C=C aromatic ring in lignin respectively. Sugarcane bagasse cellulose shows peaks at 1720.2 that represent COOH and hemicellulose carboxylic groups, while the others were not found. The crystallinity index of Nano cellulose was 42.65%. Nano cellulose film prepared in several concentrations (3%, 6%, and 9%). Nano cellulose film also prepared with adding HPMC 2%. Nano cellulose film prepared in 9% concentration was too strict and broken easily. The tensile strength and elongation of Nano cellulose film that prepared in 3% + HPMC 2% and 6% + HPMC 2% were 3.177 Mpa, 10.93% and 3.315 Mpa dan 3.7% respectively

Item Type: Conference (Paper)
Subjects: 03 CHEMICAL SCIENCES > 0301 Analytical Chemistry > 030107 Sensor Technology (Chemical aspects)
03 CHEMICAL SCIENCES > 0305 Organic Chemistry > 030502 Natural Products Chemistry
Divisions: Faculty of Medical and Health Sciences > Department of Pharmacy
Depositing User: Begum Fauziyah
Date Deposited: 24 Jun 2021 08:35

Downloads

Downloads per month over past year

Origin of downloads

Actions (login required)

View Item View Item